Details of GSAS fit for Al2O3 676a data may14/11bmb_4714

# File no. =               4714 
# No. steps =             34500 
# Scan time =             MAY 31, 2014 22:53 
# Sample name =     	  NIST SRM 676a (Al2O3) 
# Composition =           Aluminium Oxide (Al2O3)
# Sample Comment =        0.8 mm dia Kapton
# Temp (K) =              295.6 
# Temp (K) =              295.0 
# 2theta step (deg) =     0.001 
# Time per step (sec) =   0.1 
# 100/Ring Current[0] =   0.983  
# Monitor I0 [0] =        92715.5  
# Monitor I1 [0] =        75723.2  
# Gonio._radius [mm] =    1000.0 
# Calibration file =      11bmb_4699_2thcorr.calib 
# 2Theta correction subtracted 
# Normalization factor  = 8.3433 
# Calibrated wavelength = 0.413671 


GSAS Fit Summary of 11-BM Al2O3 676 Data 
# by Matthew Suchomel at APS/ANL, 2014

Using GSAS/EXPGUI
**************************************
lattice a =       4.75937 (refined)
 SRM lattice a  = 4.75909 A
 Delta lattice a from SRM = 0.0003 A

lattice c =       12.99249 (refined)
 SRM lattice c  = 12.99178 A
 Delta lattice c from SRM = 0.0007 A

Al X,Y,Z = 0.000000  0.000000  0.352114   (refined)
Al Uiso = 0.0035
O X,Y, Z, =0.693726  0.000000  0.250000   (refined)
O Uiso = 0.0035

background = 6-term Shifted Chebyschev (type #1)
GSAS Profile type 4
GU = 1.32  (refined) 
GV = -0.29 (refined) 
GW = 0.04 (refined) 
LX = 0.73 (refined, NIST SRM does not give a particle size)
S1 = 2.758E-02    (refined)
S2 = 2.603E-04    (refined)
S3 = 3.330E-03    (refined)
SH/L = 0.0011 (FIXED)

2th zero (deg) =  0.0000 (refined)
Absorption (mR/L) = 0.0 (FIXED)

Rwp % = 10.1%
chi**2 = 1.4